Harris® Harris® 0 0620FMPOP Brazing Alloy, 0.05 x 0.125 in Dia, 20 in L, Brass For Joining
- Manufacturer: The Lincoln Electric Company
- Brand Name: Harris®
- Part#: HRS0620FMPOP
- MPN: 0620FMPOP
- Min. Order Qty: 1
- Qty. Interval: 1
-
Availability:
- Branch Availability
-
Price:
-
Other Branch Availability
Harris® 0 phos-copper brazing filler metal is a low cost alloy use for many copper-to-copper applications where moderate fit-up can be maintained and brazing temperature is not critical. Complies with the EU Reach & RoHS directive.
Harris® Brazing Alloy, 7 Stick, Tube, 0.05 x 0.125 in Dia, 20 in Length, Composition: Copper, Phosphorus, Brass For Joining Material
| Additional Information | : | 19.2 uOhm Electrical Resistivity |
| Alloy Type | : | PhosCopper |
| Brazing Temperature Range | : | 1345 deg F-1500 deg F (729 deg C-816 deg C) |
| Chemical Composition | : | Copper Remainder% |
| Composition | : | Copper, Phosphorus |
| Container Size | : | 7 Stick |
| Container Type | : | Tube |
| Diameter | : | 0.05 x 0.125 in |
| Electrical Conductivity (%IACS) | : | 9.9 |
| Electrical Resistivity (Microhm/Cm) | : | 19.2 |
| Fluidity Rating | : | 5 |
| For Joining Material | : | Brass |
| Length | : | 20 in |
| Liquidus | : | 1460 deg F (793 deg C) |
| ModelName | : | HARRIS® 0 POP |
| Recommended Flux | : | No flux required for copper brazing. For brazing brass or copper to brass use Stay-Silv white flux. When flux is required, Harris Eco Smart boric acid free flux (powder or paste) is an excellent choice to promote sound brazed assemblies and comply with European REACH requirements. |
| Recommended Joint Clearance | : | .002"-.007" (.051mm-.178mm) |
| Shape | : | Stick |
| Size | : | 7 stick tube |
| Solidus | : | 1310 deg F (710 deg C) |
| Temperature Rating | : | 1345 to 1500 deg F |
- Economical choice for copper brazing
- Copper is self-fluxing, so no manual flux application is required
- Alloy flows quickly at brazing temperature requiring close joint tolerance, less than 0.005 in. (0.13 mm)
- Primarily used in manual brazing applications
- Suitable for brazing brass
- When brazing brass, operators should avoid over heating and use Stay Silv® white brazing flux
- Not recommended for brazing steel or other ferrous base metals
- Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including Harris® 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service
- Recommended joint clearance of 0.002 in. - 0.005 in. (0.05 mm - 0.13 mm)
- Complies with the EU Reach & RoHS directive
Specification Sheet