Harris® 15 Series 015FC600POP Low-Fuming Flux-Coated Brazing Alloy, 1/8 in Dia, 36 in L, Bronze
- Manufacturer: The Lincoln Electric Company
- Brand Name: Harris®
- Part#: HRS015FC600POP
- MPN: 015FC600POP
- Min. Order Qty: 1
- Qty. Interval: 1
-
Availability:
- Branch Availability
-
Price:
-
Other Branch Availability
Harris® 15 low fuming bronze (LFB) flux-coated is considered a "braze-welding" alloy as this copper/zinc alloy exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure alloy penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and gray iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process. This alloy is flux-coated, eliminating the need for manual flux application.
Harris® Low-Fuming Flux-Coated Brazing Alloy, 15 Series, 4 lb Net Content, Box Container, 1/8 in Diameter, 36 in Length, Composition: Tin, Copper, Iron, Manganese, Silicon, Zinc, Lead, Aluminum, Finish: Bronze, For Joining Material: Steel, Cast Iron, Malleable and Gray Iron, Copper, Additional Information: Copper Zinc Material
| Additional Information | : | Copper Zinc Material |
| Alloy Type | : | CopperBased |
| Brazing Temperature Range | : | 1670 deg F-1750 deg F (910 deg C-954 deg C) |
| Chemical Composition | : | Tin 0.80-1.10%;Copper 56-60%;Iron 0.25-1.20%;Manganese 0.01-0.50%;Silicon 0.04-0.15%;Zinc Remainder% |
| Color | : | Yellow brass |
| Composition | : | Tin, Copper, Iron, Manganese, Silicon, Zinc, Lead, Aluminum |
| Container Size | : | 1 lb |
| Container Type | : | Box |
| Diameter | : | 1/8 in |
| Finish | : | Bronze |
| For Joining Material | : | Steel, Cast Iron, Malleable and Gray Iron, Copper |
| Length | : | 36 in |
| Liquidus | : | 1630 deg F (888 deg C) |
| ModelName | : | HARRIS® 15 LFB-FC White POP |
| Net Content | : | 4 lb |
| Recommended Flux | : | No flux required |
| Series | : | 15 Series |
| Shape | : | Rod |
| Size | : | 1 lb. pkg. |
| Solidus | : | 1590 deg F (866 deg C) |
| Temperature Rating | : | 1670 to 1750 deg F |
- Copper-zinc braze-welding flux-coated rod using oxy-fuel
- Flux coating provides excellent wetting action with no objectionable fuming
- Exhibits minimal capillary action during brazing
- Limited joint designs to lap, tee and butt joints, although butt joints require some edge preparation
- Good machinability
- Produces porosity-free deposits
- Good color match to brass
- Developed to braze steel and some cast iron grades including malleable and gray iron and joining copper
- Corrosion resistance is similar to most high zinc brass alloys. Care should be taken on service conditions where water immersion is involved as dezincification is a potential issue.
- Conveniently packaged for point-of-purchase display